SHEET BUILDING GLASS WITH PROTECTIVE AND DECORATIVE COATINGS

https://doi.org/10.34031/2618-7183-2019-2-1-11-16
Abstract
Sheet glass with decorative coatings in industrial and civil construction play an important role in improving the aesthetic properties of buildings for various purposes. An innovative technology for obtaining decorative coatings on sheet glasses using low-temperature plasma is proposed. For plasma spraying crushed in a ball mill container glass of various colors was used. The optimal parameters of the plasma spraying of glass powders on the front surface of the glass sheets were established. To increase the adhesion strength of the coating to the substrate before plasma spraying, the front surface was heat treated with outgoing plasma-forming gases. It was found that with increasing temperature of the outgoing plasma-forming gases and the time of their impact on the front surface of the sheet glass, the adhesion strength of the coating with the base increases to 6.7 MPa. The effect of the coating thickness on the strength of its adhesion to the substrate is studied. Increasing the coating thickness from 150 to 1000 µm reduces the adhesion strength from 7.5 to 3.2 MPa. Under the influence of high temperatures of arc plasma is not only an increase in the glass refractory oxides of silicon and aluminum, but also an increase in their hardness up to 15%.
PDF

VITREOUS PROTECTIVE AND DECORATIVE COVERINGS ON WOOD PARTICLE BOARD

https://doi.org/10.34031/2618-7183-2018-1-4-4-12
Abstract
Scientific and technological bases of receiving vitreous coverings on wood with use of a torch of low-temperature plasma are developed. Before plasma dusting of glass powders by grain structure 60-120mkm, the special protective coating protecting chipboard from destruction at high-temperature influence of a plasma stream on a front surface of the wood particle board (WPB) was applied. The structure of an intermediate protective coating including mix of a fine-grained glass powder and liquid glass is developed. Preliminary drawing an intermediate protective layer provides several consecutive technological operations.
For receiving vitreous coverings fight of colored and colourless glass are used which was previously ground in spherical porcelain mills. Optimum process parameters of plasma dusting of glass powder on the front surface of chipboard are developed. Optimum parameters of plasma melting is: current - 800A; operating voltage – 30B, a consumption of plasma-forming gas of argon 2m3/h.
Operational and aesthetic-consumer properties of vitreous protective and decorative coverings are investigated. It is established that vitreous protective and decorative coverings have the high durability of coupling with an intermediate protective layer. The received vitreous protective and decorative coverings on the basis of colored and colourless glass have the high water resistance, acid resistance, alkali resistance, as well as microhardness and high aesthetic performance.
The technology is recommended for widespread industrial introduction.