Alehin D.A.

Postgraduate, Belgorod State Technological University named after V.G. Shukhov, Russia

THEORETICAL ASPECTS OF DEVELOPMENT OF COMPOSITE NANOSTRUCTURED GYPSUM BINDER CHARACTERIZED BY INCREASED HEAT RESISTANCE

https://doi.org/10.34031/2618-7183-2019-2-4-5-13
Abstract
There are a lot of different types of binders for construction purpose, a strong interest is focused on free-of-cement binders of new generation, which are characterized by unique and/or improved performance proper-ties. Among them there is composite nanostructured gypsum binder (CNGB) as a quite new binding system. In the framework of this study the hypothesis of synergetic effect in hardened binding system was proposed and approved. The hypothesis is realized when interaction of two binding systems with different structure formation mechanism such as followings: polymerization-polycondensation and hydration. A number of experiments were carried out and the results were obtained, which demonstrate a resistance of CNGB under high-temperature effect (up to 1000ºC) vs. ordinary gypsum binder. It was determined that a heat-resistance of CNGB is associated with joint crystallization of sulphate-based component (gypsum binder) and highly-reactive silica-based component (in nanostructured binder). Normally, nanostructuted binder is stable under high-temperature exposure. The indicator of synergetic effect is formation of new crystalline phase – hydroxyellestadite Ca5(SiO4)3(SO4)3(OH)2. This phase has unit cell size which is stable under temperature gradient. This characteristic allows saving structure framework in CNGB under high temperature.
PDF