The paper discusses the development of alkali-activated binders based on technogenic fibrous materials. An approach to the secondary use of technogenic fibrous materials as a filler of composite binders is offered. The properties of mineral wool waste have been established. The microstructure of finely ground fibrous particles has been studied. Compositions of alkali-activated binders were de-veloped, when grinding basalt insulation production waste to a specific surface of 300-330 m2 /kg, followed by the formation of a binder according to the first method with rod tamping sealing and, ac-cording to the second, by pressing a raw binder mixture at a pressure of 10 MPa. The developed com-positions of alkali–activated binder by pressing with a compressive strength of 22.8 MPa, and when compacted with subsequent rod tamping – 11.8 MPa.